1.Wear resistance with good stiffness
2.High toughness
3.Heat resistance
4.Low difficulty of printing
5.Low wrapping and good thermal stability
6.Easy to print
7.Eco-friendly
8.Corrosion resistance, oil resistance, excellent mechanical properties
Dimensions：1.75mm/2.85mm
Weight of each roll：1kg/2kg
| Property | Testing Method | Testing Condition | Injection Molding Typical Value | 3D Printing X-Y Axis Typical Value | 3D Printing Z Axis Typical Value | Unit |
| Tensile Strength | ISO 527 | 50mm/min | 65.1 | 59±4 | 27±4 | MPa |
| Elongation at Break | ISO 527 | 50mm/min | 3.6 | 2±1 | 1.1±0.2 | % |
| Tensile Modulus | ISO 527 | 50mm/min | 2592.1 | 2207±200 | 1863.7±200 | MPa |
| Flexural Strength | ISO 178 | 2mm/min | 110.6 | 108.4±5 | 50.2±5 | MPa |
| Flexural Modulus | ISO 178 | 2mm/min | 2560 | 2335±200 | 1673.4±200 | MPa |
| Charpy Impact Strength | ISO 179 | 23℃ | 37.2 | 10.4±2 | 3.3±1 | KJ/㎡ |
| Izod Impact Strength | ISO 180 | 23℃ | 33.1 | 8.6±2 | 2.1±1 | KJ/㎡ |
| Property | Testing Method | Testing Condition | Typical Value | Unit |
| Density | ISO 1183 | Immersion | 1.13 | g/cm3 |
| Melt Flow index(MFR) | ISO 1133 | 275℃/2.16kg | 8-18 | g/10 min |
| Property | Testing Method | Testing Condition | Injection Molding Typical Value | 3D Printing Typical Value | Unit |
| Moisture Absorption | ISO 62 | 50%RH*23℃ | 2.5 | 2.7 | % |
| Property | Testing Result |
| Weak Acid Resistance | Not Resistant |
| Strong Acid Resistance | Not Resistant |
| Weak Base Resistance | Lightly Resistant |
| Strong Base Resistance | Not Resistant |
| Organic Solution Resistance | Not Resistant |
| Oil and Grease Resistance | Resistant |
| Property | Testing Method | Testing Condition | Injection Molding Typical Value | 3D Printing X-Y Axis Typical Value | 3D Printing Z Axis Typical Value | Unit |
| Glass Transition Temperature | DSC | 10℃/min | 53.7 | ℃ | ||
| Crystallization temperature | DSC | 10℃/min | 179.8 | ℃ | ||
| Melting Point | DSC | 10℃/min | 221.9 | ℃ | ||
| Distortion Temperature | TGA | 20℃/min | ＞370 | ℃ | ||
| Heat Distortion Temperature | ISO 75 | 0.45MPa | 72.8 | 69.7 | 57.4 | ℃ |
| Heat Distortion Temperature | ISO 75 | 1.8MPa | 62.5 | 59.2 | 50.6 | ℃ |
| Vicat Softening Temperature | ISO 306 | 50℃/10N | N/A | ℃ | ||
| Printing Temperature | 250-280(℃) |
| Bed Temperature | 80-100(℃) |
| Wall Layers | 2 Layers |
| Top and Bottom Layers | 4 Layers |
| Infill | 100% |
| Ambient Temperature | 25℃ |
| Cooling Fan | 0-10% |
| Printing Speed | 30-50(mm/s) |
| Nozzle Diameter | 0.4 mm |
| Printing Temperature | 260(℃) |
| Bed Temperature | 80(℃) |
| Wall Layers | 2 Layers |
| Top and Bottom Layers | 4 Layers |
| Infill | 100% |
| Ambient Temperature | 25℃ |
| Cooling Fan | 10% |
| Printing Speed | 50(mm/s) |
| Nozzle Diameter | 0.4 mm |
Jiangyin Longshan Synthetic Materials Co., Ltd. is a modified plastics company integrating R&D, production and sales, specializing in the development of medium and high-end modified materials.