PPS-CF

Material Type

PPS-CF
Product Specification

Dimensions：1.75mm/2.85mm
Weight of each roll：1kg/3kg

Color

Carbon Fiber Black

Aliz PPS-CF 3D PRINTING FILAMENT

PPS-CF
PPS-CF
PPS-CF
PPS-CF
Powerful Performance To Bring Your ldeas To Life

PPS-CF ADVANTAGES

Inherent Flame Retardancy

Inherent Flame Retardancy

It can achieve UL94 V-0 grade without the addition of flame retardants, providing intrinsically safe features for applications with strict fire protection requirements.

Ready-to-Use Matte Finish

Ready-to-Use Matte Finish

Producing components with a uniform, professional-grade matte surface that is both aesthetically pleasing and functional.

Excellent Dimensional Stability & Low Warp

Excellent Dimensional Stability & Low Warp

Its low shrinkage and thermal expansion coefficient, combined with a formulation optimized for open-chamber printing at high bed temperatures, enable the production of large, precise parts with minimal warping.

High Strength & Stiffness at High Temperatures

High Strength & Stiffness at High Temperatures

Carbon Fiber reinforcement significantly enhances tensile strength and rigidity, and its performance can still be maintained at temperatures above 200℃, with excellent creep resistance.

Superior Chemical Resistance

Superior Chemical Resistance

Exhibits outstanding resistance to oils, fuels, solvents and various corrosive chemicals. Maintains stable mechanical properties when exposed to harsh chemicalrich environments, wellsuited for chemicalcontact industrial components.

Outstanding Chemical & Hydrolytic Resistance

Outstanding Chemical & Hydrolytic Resistance

It has excellent resistance to a wide range of chemicals, acids and alkalis. Its extremely low moisture/water absorption ensures long-term dimensional stability and performance integrity in wet or humid conditions, a critical advantage over nylon-based materials.

Carbon Fiber PETG
Carbon Fiber PETG

Premium Matte Finish

Carbon fiber matte texture reduces layer lines, delivering a refined, professional finish.

Regular PETG
Regular PETG

PPS-CF APPLICATIONS

Aerospace & Defense Prototypes Aerospace & Defense Prototypes

Low Shrinkage &
No Warping

Carbon fiber improves material shrinkage on cooling and reduces warpage.

Recommended Nozzle Temperature
240-270 °C
Recommended Heated Bed Temperature
65-75 °C

Fit Most FDM 3D Printers

The all-new AMS lite is elegant and reliable, making multi-color 3D printing accessible to everyone.

Printer 1 Printer 2 Printer 3

Perfect for Demanding, High-Performance Applications

Mechanical Properties
Property Testing Method Testing Condition Injection Molding Typical Value 3D Printing X-Y Axis Typical Value 3D Printing  Z Axis Typical Value Unit
Tensile Strength ISO 527 50mm/min 103 77±4 30.5±2 MPa
Elongation at Break ISO 527 50mm/min 2.1 2±1 1.2±0.5 %
Tensile Modulus ISO 527 50mm/min 6818.2 5635.9±200 2547.9±300 MPa
Flexural Strength ISO 178 2mm/min 140.9 105±4 42±4 MPa
Flexural Modulus ISO 178 2mm/min 6705 6265±200 2863.7±300 MPa
Charpy Impact Strength ISO 179 23℃ 31 12.9±2 3.6±1 KJ/㎡
Izod Impact Strength ISO 180 23℃ 27 12.8±2 3.1±1 KJ/㎡

Physical Properties
Property Testing Method Testing Condition Typical Value Unit
Density ISO 1183 Immersion 1.27 g/cm3
Melt Flow index(MFR) ISO 1133 315℃/2.16kg 10-20 g/10 min

Moisture Absorption
Property Testing Method Testing Condition Injection Molding Typical Value 3D Printing Typical Value Unit
Moisture Absorption ISO 62 50%RH*23℃ 0.02 0.02 %

Chemical Properties
Property Testing Result
Weak Acid Resistance Resistant
Strong Acid Resistance Resistant
Weak Base Resistance Resistant
Strong Base Resistance Resistant
Organic Solution Resistance Resistant
Oil and Grease Resistance Resistant

Thermal Properties
Property Testing Method Testing Condition Injection Molding Typical Value 3D Printing X-Y Axis Typical Value 3D Printing Z Axis Typical Value Unit
Glass Transition Temperature DSC 10℃/min 89.8 ℃
Melting Point DSC 10℃/min 280.4 ℃
Distortion Temperature TGA 20℃/min ＞400 ℃
Heat Distortion Temperature ISO 75 0.45MPa 249.1 245.2 200.1 ℃
Heat Distortion Temperature ISO 75 1.8MPa 223.4 220.1 194.7 ℃
Vicat Softening Temperature ISO 306 50℃/10N N/A ℃

Recommended 3D Printing Parameters
*Based on 0.4 mm nozzle. Printing conditions may vary with different nozzle diameters.
Printing Temperature 300-350(℃)
Bed Temperature 100(℃)
Wall Layers 2 Layers
Top and Bottom Layers 4 Layers
Infill 100%
Ambient Temperature 25℃
Cooling Fan 0-10%
Printing Speed 30-50(mm/s)
Nozzle Diameter 0.4 mm

3D Printing Actual Parameters
*All specimens must be left at room temperature for 24 hours before testing. The parameters are based on the Bambulab P1S 3D printer.
Printing Temperature 330(℃)
Bed Temperature 100(℃)
Wall Layers 2 Layers
Top and Bottom Layers 4 Layers
Infill 100%
Ambient Temperature 25℃
Cooling Fan 10%
Printing Speed 50 (mm/s)
Nozzle Diameter 0.4 mm
Jiangyin Longshan Synthetic Material Co., Ltd.

Longshan specializes in the R&D and production of modified plastic pellets. Aliz is its subsidiary, focusing exclusively on 3D printing consumables.