1. Enhanced Toughness
2. Better Layer Adhesion
3. More Matte Finish Look
Dimensions：1.75mm/2.85mm
Weight of each roll： 1kg/2.5kg
| Property | Testing Method | Testing Condition | Injection Molding Typical Value |
3D Printing X-Y Axis Typical Value |
3D Printing Z Axis Typical Value |
Unit |
| Tensile Strength | ISO 527 | 50mm/min | 50.95 | 48.96±4 | 26±4 | MPa |
| Elongation at Break | ISO 527 | 50mm/min | 13 | 7±1 | 0.75±0.2 | % |
| Tensile Modulus | ISO 527 | 50mm/min | 5549 | 3325±100 | 3100±100 | MPa |
| Flexural Strength | ISO 178 | 2mm/min | 77.33 | 78.5±5 | 44±5 | MPa |
| Flexural Modulus | ISO 178 | 2mm/min | 3127.50 | 2920±100 | 2550±100 | MPa |
| Charpy Impact Strength Without Notch | ISO 179 | 23℃ | NB | 15.5±2 | 8.5±2 | KJ/㎡ |
| Izod Impact Strength Without Notch |
ISO 180 | 23℃ | 83.05 | 16.8±2 | 8.5±2 | KJ/㎡ |
| Property | Testing Method | Testing Condition | Typical Value | Unit |
| Density | ISO 1183 | Immersion | 1.24 | g/cm3 |
| Melt Flow index(MFR) | ISO 1133 | 210℃/2.16kg | 5-15 | g/10 min |
| Property | Testing Method | Testing Condition | Injection Molding Typical Value | 3D Printing Typical Value | Unit |
| Moisture Absorption | ISO 62 | 50%RH*23℃ | 0.5 | 0.6 | % |
| Property | Testing Result |
| Weak Acid Resistance | Not Resistant |
| Strong Acid Resistance | Not Resistant |
| Weak Base Resistance | Not Resistant |
| Strong Base Resistance | Not Resistant |
| Organic Solution Resistance | Not Resistant |
| Property | Testing Method | Testing Condition | Injection Molding Typical Value | 3D Printing X-Y Axis Typical Value |
3D Printing Z Axis Typical Value |
Unit |
| Glass Transition Temperature | DSC | 10℃/min | 65.51 | ℃ | ||
| Crystallization Temperature | DSC | 10℃/min | 107.7 | ℃ | ||
| Melting Point | DSC | 10℃/min | 147.77 | ℃ | ||
| Distortion Temperature | TGA | 20℃/min | N/A | ℃ | ||
| Heat Distortion Temperature | ISO 75 | 0.45MPa | 57.6 | 56.20 | 55.20 | ℃ |
| Heat Distortion Temperature | ISO 75 | 1.8MPa | 56.4 | 54.20 | 53.20 | ℃ |
| Vicat Softening Temperature | ISO 306 | 50℃/10N | 56.60 | 57.80 | 56.40 | ℃ |
| Printing Temperature | 270-300(℃) |
| Bed Temperature | 80-100(℃) |
| Wall Layers | 2 Layers |
| Top and Bottom Layers | 4 Layers |
| Infill | 100% |
| Ambient Temperature | 25℃ |
| Cooling Fan | 0-10% |
| Printing Speed | 30-50(mm/s) |
| Nozzle Diameter | 0.4 mm |
| Printing Temperature | 280(℃) |
| Bed Temperature | 100(℃) |
| Wall Layers | 2 Layers |
| Top and Bottom Layers | 4 Layers |
| Infill | 100% |
| Ambient Temperature | 25℃ |
| Cooling Fan | 10% |
| Printing Speed | 50(mm/s) |
| Nozzle Diameter | 0.4 mm |
Jiangyin Longshan Synthetic Materials Co., Ltd. is a modified plastics company integrating R&D, production and sales, specializing in the development of medium and high-end modified materials.